Study of vortex pinning by development of normal-superconducting interfaces oriented on a nanometric scale within a superconducting NBTI alloy

par Xianghong Liu

Thèse de doctorat en Physique

Sous la direction de Lian Zhou et de André Sulpice.

Soutenue en 2004

à l'Université Joseph Fourier (Grenoble) en cotutelle avec Northeastern University, Shenyang, China .

    mots clés mots clés


  • Résumé

    Durant l'etirage, des defauts artificiels (apc) de nb et de ti5%nb introduits dans des fils de nbti se deforment progressivement en rubans. Pour les composites avec des defauts de nb sous forme de barrieres ou d'iles, un pic de la force de piegeage fp apparait entre 3 et 5 t, alors que pour les apc en couches, le pic se situe entre 1 et 2 t. Les composites en iles ont de meilleures performances a haut champ a cause du plus grand nombre de pieges. Pour les composites avec des apc de ti5%nb, l'augmentation du nombre d'inclusions conduit a une reduction de hc2 et de tc a cause des effets de proximite. Lorsque les conducteurs sont lamines sous forme de rubans, le courant critique jc// depasse 4155 a/mm2 a 5 t et 4. 2 k. Pour les composites avec des defauts de nb, un traitement thermique augmente jc a fort champ mais reduit les performances a bas champ, ce qui est exactement l'inverse pour les composites avec des defauts ti5%nb.


  • Pas de résumé disponible.

  • Titre traduit

    Etude du piégeage des vortex par le développement d'interfaces normales orientées à une échelle nanométrique dans les alliages de NTBI supraconducteur


  • Résumé

    Different original shapes of nb and ti5%nb artificial pins are gradually deformed into ribbon-like structure during wire drawing process. For nb apc composites, that is, barrier-shaped and island-shaped apc composites, fp peaks appear at the fields from 3 to 5t. The layer-shaped nb apc composites show fp peaks at the fields from 1 to 2t. Island-shaped nb apc composite has a higher performance at higher fields due to higher number density of apc and their interfaces. For ti-5%nb apc composites, more content of pins give rise to the reduction of both hc2 and tc due to proximity effect, and then the high field performance is reduced. As the apc composite wires with nb island-shaped apc are rolled into tapes, the parallel jc// values are more than 4155a/mm2 at 5t, 4. 2k when nbti/cu tapes are parallel to magnetic fields. For nb apc composites, heat treatment improved the high field jc and fp, however, the low field jc and fp were reduced obviously. By contrast, the low field jc and fp were improved and the high field jc and fp were reduced in nbti composites with ti5nb apc after heat treatment.

Consulter en bibliothèque

La version de soutenance existe sous forme papier

Informations

  • Détails : VII-160 p.
  • Notes : Publication autorisée par le jury
  • Annexes : Bibliogr. p.151-160

Où se trouve cette thèse ?

  • Bibliothèque : Service interétablissements de Documentation (Saint-Martin d'Hères, Isère). Bibliothèque universitaire de Sciences.
  • Non disponible pour le PEB
  • Cote : TS04/GRE1/0087
  • Bibliothèque : Service interétablissements de Documentation (Saint-Martin d'Hères, Isère). Bibliothèque universitaire de Sciences.
  • Disponible pour le PEB
  • Cote : TS04/GRE1/0087/D
Voir dans le Sudoc, catalogue collectif des bibliothèques de l'enseignement supérieur et de la recherche.